Engineered composite systems

ABSTRACT

A system for providing improved engineered-composite materials, equipment, and manufacturing processes.

CROSS-REFERENCE TO RELATED APPLICATIONS

This U.S. Continuation Applications claims priority to U.S. Non-Provisional patent application Ser. No. 14/207,790, which was filed on Mar. 13, 2014, entitled “ENGINEERED COMPOSITE SYSTEMS” which claims priority to U.S. Provisional Patent Application Ser. No. 61/780,345 filed Mar. 13, 2013 entitled “ENGINEERED COMPOSITE SYSTEMS”, all of which is hereby incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION

Related disclosures are found in U.S. Pat. No. 5,470,062, entitled “COMPOSITE MATERIAL FOR FABRICATION OF SAILS AND OTHER ARTICLES,” which was issued on Nov. 28, 1995; and U.S. Pat. No. 5,333,568, entitled “MATERIAL FOR THE FABRICATION OF SAILS” which was issued on Aug. 2, 1994; and U.S. patent application Ser. No. 13/168,912, filed Jun. 24, 2011 entitled “WATERPROOF BREATHABLE COMPOSITE MATERIALS FOR FABRICATION OF FLEXIBLE MEMBRANES AND OTHER ARTICLES,”; and U.S. patent application Ser. No. 13/197,741, filed Aug. 3, 2011 entitled “SYSTEM AND METHOD FOR THE TRANSFER OF COLOR AND OTHER PHYSICAL PROPERTIES TO LAMINATE COMPOSITE MATERIALS AND OTHER ARTICLES”, the contents of all of which are hereby incorporated by reference for any purpose in their entirety.

This invention relates to improved flexible composite systems. More particularly, this invention relates to a system for quickly and economically producing high-quality engineered-composite materials exhibiting enhanced “stretch” properties, or modulus attained, or rebound ability. Such composites would be of benefit within many technical fields.

Further, this invention relates to providing improved monofilament-related products, methods, and equipment. More particularly, this invention relates to providing systems for design and manufacture of products using the technologies and useful arts herein taught and embodied. Even more particularly, this invention provides improvements in efficiently controlling properties of fabric-related products, including but not limited to: weight, rigidity, penetrability, waterproof-ability, breathability, color, mold-ability, cost, customizability, flexibility, package-ability, etc., including desired combinations of such properties.

In the past, there has been difficulty in achieving desired combinations of such properties, especially with regard to fabric-related products like clothing and shoes, camping and hiking goods, comfortable armor, protective inflatables, etc.

OBJECTS AND FEATURES OF THE INVENTION

A primary object and feature of the present invention is to provide a system overcoming the above-mentioned problem.

Another primary object and feature of the present invention is to provide a system to fine-tune, at desired places on a product, directional control of rigidity/flexibility/elasticity properties.

Yet another primary object and feature of the present invention is to provide products combining extreme light weight with extreme strength.

A further primary object and feature of the present invention is to provide such a system that is efficient, inexpensive, and handy. Other objects and features of this invention will become apparent with reference to the following descriptions.

SUMMARY OF THE INVENTION

In accordance with a preferred embodiment hereof, this invention provides a laminate including reinforcing elements therein, such reinforcing elements including at least one unidirectional tape having monofilaments therein, all of such monofilaments lying in a predetermined direction within the tape, wherein such monofilaments have diameters less than 20 microns and wherein spacing between individual monofilaments within an adjoining strengthening group of monofilaments is within a gap distance in the range between non-abutting monofilaments up to nine times the monofilament major diameter.

Moreover, it provides such a laminate wherein such monofilaments are extruded. Additionally, it provides such a laminate wherein such reinforcing elements include at least two unidirectional tapes, each having extruded monofilaments therein, all of such monofilaments lying in a predetermined direction within the tape, wherein such monofilaments have diameters less than 20 microns and wherein spacing between individual monofilaments within an adjoining strengthening group of monofilaments is within a gap distance in the range between non-abutting monofilaments up to nine times the monofilament major diameter. Also, it provides such a laminate wherein each of such at least two unidirectional tapes includes larger areas without monofilaments therein and wherein such larger areas comprise laminar overlays comprising smaller areas without monofilaments.

In addition, it provides such a laminate wherein such smaller areas comprise user-planned arrangements. And, it provides such a laminate further comprising a set of water-breathable elements comprising laminar overlays of such smaller areas. Further, it provides such a laminate further comprising a set of other laminar overlays. Moreover, it provides such a laminate wherein a first one of such at least two unidirectional tapes includes monofilaments lying in a different predetermined direction than a second one of such at least two unidirectional tapes.

Additionally, it provides such a laminate wherein a combination of the different predetermined directions of such at least two unidirectional tapes is user-selected to achieve laminate properties having planned directional rigidity/flexibility. Also, it provides such a laminate comprising a three-dimensionally shaped, flexible composite part. In addition, it provides such a product comprising multiple laminate segments attached along peripheral joints. And, it provides such a product comprising at least one laminate segment attached along peripheral joints with at least one non-laminate segment. Further, it provides such a product comprising multiple laminate segments attached along area joints.

Even further, it provides such a product comprising at least one laminate segment attached along area joints with at least one non-laminate segment. Moreover, it provides such a product comprising at least one laminate segment attached along area joints with at least one unitape segment. Additionally, it provides such a product comprising at least one laminate segment attached along area joints with at least one monofilament segment. Also, it provides such a product further comprising at least one rigid element.

In accordance with another preferred embodiment hereof, this invention provides a product wherein such at least one unidirectional tape is attached to such product. In accordance with a preferred embodiment hereof, the present system provides each and every novel feature, element, combination, step and/or method disclosed or suggested by this patent application.

Brief Glossary of Terms and Definitions

-   Adhesive: A curable resin used to combine composite materials. -   Anisotropic: Not isotropic; having mechanical and or physical     properties which vary with direction at a point in the material. -   Aerial Weight: The weight of fiber per unit area, this is often     expressed as grams per square meter (g/m²). -   Autoclave: A closed vessel for producing an environment of fluid     pressure, with or without heat, to an enclosed object which is     undergoing a chemical reaction or other operation. -   B-stage: Generally defined herein as an intermediate stage in the     reaction of some thermosetting resins. Materials are sometimes pre     cure to this stage, called “prepregs”, to facilitate handling and     processing prior to final cure. -   C-stage: Final stage in the reaction of certain resins in which the     material is relatively insoluble and infusible. -   Cure: To change the properties of a polymer resin irreversibly by     chemical reaction. Cure may be accomplished by addition of curing     (cross-linking) agents, with or without catalyst, and with or     without heat. -   Decitex (DTEX): Unit of the linear density of a continuous filament     or yarn, equal to 1/10th of a tex or 9/10th of a denier -   Dyneema™ Ultra-high-molecular-weight polyethylene fiber by DSM -   Filament: The smallest unit of a fiber-containing material.     Filaments usually are of long length and small diameter. -   Polymer: An organic material composed of molecules of monomers     linked together. -   Prepreg: A ready-to-cure sheet or tape material. The resin is     partially cured to a B-stage and supplied to a layup step prior to     full cure. -   Tow: An untwisted bundle of continuous filaments. -   UHMWPE: Ultra-high-molecular-weight polyethylene. A type of     polyolefin made up of extremely long chains of polyethylene. Trade     names include Spectra® and Dyneema® -   Unitape Uni-Directional tape (UD tape)—flexible reinforced tapes     (also referred to as sheets) having uniformly-dense arrangements of     reinforcing fibers in parallel alignment and impregnated with an     adhesive resin. UD tape are typically B-staged and form the basic     unit of most CT composite fabrics.

BRIEF DESCRIPTION OF THE DRAWING FIGURES

FIG. 1A is an illustration of S06 where A is the fiber, B is the matrix and C is the woven material, note there is no top or bottom coating; and

FIG. 1B is an illustration of S07 and S13 where A is the fiber and B is the matrix material, C in this FIGURE preferably comprises a waterproof non-breathable urethane film.

DETAILED DESCRIPTION

TABLE 1 Sample Delamination rank after ½ Sample hour wash/ weight Layer Layer Layer Layer Layer Additional Comments Number durability translucence (gsm) 1 2 3 4 5 comments white woven S06 3 4 64 release liner #538 WHC #538 release liner Non-waterproof inner layer no removed 0° 2 90° removed breathable outer coatings after after and natural process process color, 0/90 fibers, moderate air permeable no coating one S07 5 4 92 W2-1.0 #5380°  #5380° release liner Waterproof side, coated on removed Non-breathable the other, 0/60 after fiber, natural process color no coating one S13 4 4 90 W2-1.0 #1420° #14260° release liner Waterproof side, coated on removed Non-breathable the other, 0/60 after fiber, grey process

Each of the materials of Table (1) preferably utilize Unitape layers. A preferred Unitape layers is preferably manufactured by spreading fibers and coating them with an adhesive to form a substantially continuous sheet. The preferred Unitape layers are non-woven.

More specifically, each of the flexible sheet materials of Table (1) preferably utilizes Unitape layers (either applicant's #538 or #142 Unitape). Preferably, these unitape “sheets” are cut to size and layed in multiple orientations to form a preferred two directional fiber reinforced sheet. Each of the materials of Table (1) preferably utilize Unitape layers (either #538 or #142) with following preferred characteristics:

-   -   About 14 gsm of non-breathable CT71 adhesive in the unitape and         14 gsm of Dyneema SK75 1760Dtex fiber, which, when cross plied,         preferably creates a fiber matrix network that will bead water         and will be air permeable but will allow water to pass through         with significant atmospheric pressure.     -   Unitape #142 has a small amount of light grey tint in the CT71         adhesive that makes the resulting products have a light grey         color.     -   Unitape #538 is natural colored (translucent pale yellow) so the         resulting products are translucent pale yellow.

As illustrated in FIGS. 1A and 1B, laminate S06 has no film or membrane on either side of the laminate but has the woven material we have coded as WHC2 (Nylon 6 ripstop, 10d×10d+30d, 255×218, 26 g/sqm, C6:DWR) sandwiched between the unitape layers, the purpose of the woven is to add rip-stop performance to the laminate and add structural stability to the laminate. This material is a typical 0/90° orientation but has lower than normal modulus in the +/−45° directions because of the lack of film or membrane Laminate S07 does not have a film or membrane on one side but has a non-breathable urethane membrane film W2−1.0 on the other side so that it is waterproof-non breathable with fibers laid at about 0° and 60° so the material (through the combination of the fiber angles and stretchable film) has low modulus in the 120° direction and moderate modulus in the 30° direction Laminate S13 is same as S07 but is light grey because of the unitape used.

The “membrane-free” flexible composite generally exhibits greater “stretch”, or modulus attained, or rebound ability (of the materials in the non-fiber reinforced directions), when compared to applicant's prior-disclosed embodiments (see U.S. Pat. No. 5,470,632 to Heiner Meldner et al). Applicant's new disclosed embodiments are preferably designed to have a low modulus or rebound in the off axis directions.

It is noted that applicant's preferred adhesive coating (CT71) is preferably a partially thermosetting polymer that has excellent adhesion to low surface energy fibers (and films, as applicable) and forms a toughened finished product once cured that is puncture resistant and resists UV degradation. Upon reading this specification, those with ordinary skill in the art will now appreciate that, under appropriate circumstances, considering such issues as design preference, intended use, cost, structural requirements, available materials, technological advances, etc., other laminate versions, such as, for example, a non-breathable membrane applied on one or both sides of the layup assembly, which preferably could be replaced with breathable membranes.

In another preferred embodiment of the present invention, materials have an engineered stretch wherein the finished material stretch and rebound and design directions may be used in designed amounts. For example, a flexible composite with a high modulus from initial strain in the X-Y plain directions 0°/180°, 90°/270°, and 45°/225° but lower strengths, from initial strain, in all other x-y plane directions.

Preferably, the initial modulus of the material drops off as the direction of stress moves farther and farther from a fiber reinforced direction and increases as the load moves back towards a fiber reinforced direction. By knowing the material characteristics of each component ply and the interaction effects they have with each other a material can be manufactured with particular characteristics that may be drastically different than the constituent components.

The following table discloses Unitape layers (applicant's #538 Unitape). Preferably, these unitape “sheets” are cut to size and layed in multiple orientations to form a preferred multi-directional fiber reinforced sheet. Each of the materials of Table (2) preferably utilize Unitape layers (either #538) in angular orientation (0-degrees; 45-degrees) with following preferred characteristics, as shown:

Product Sample Aprox. name Number weight (gsm) Layer 1 Layer 2 Layer 3 Layer 4 Layer 5 CT9BW6-2.0 (45) S40 215 W6-2.0 #538 0° #538 45° #538 −45° W6-2.0 CT9BW2- S45 163 Tricot knit #538 0° #538 45° #538 −45° W2-1.0 1.0/TR1 (45) (any

Preferably, each of the materials above preferably utilize Unitape layers. Preferred Unitape layers are preferably manufactured by spreading fibers and coating them with an adhesive to form a substantially continuous sheet. The preferred Unitape layers are non woven.

More specifically, each of the flexible sheet materials of the above Table 2 preferably utilizes Unitape layers (applicant's #538 Unitape). Preferably, these unitape “sheets” are cut to size and laid in multiple orientations to form a preferred three directional fiber reinforced sheet. Each of the materials of Table (1) preferably utilize Unitape layers (#538) with the following preferred characteristics:

-   -   About 14 gsm of non-breathable CT71 adhesive in the unitape and         14 gsm of Dyneema SK75 1760Dtex fiber, which, when cross plied,         preferably creates a fiber matrix network that will bead water         and will be air permeable but will allow water to pass through         with significant atmospheric pressure.     -   Unitape #538 may include additives that cause it to become         colored to inventors desire     -   Unitape #538 is natural colored (translucent pale yellow) so the         resulting products are translucent pale yellow.

Additionally, as illustrated above, laminate S40 preferably has a non-breathable weldable urethane film W6−2.0 on both the bottom and top surfaces and three layers of #538 unitape. This material is a 0/+45/−45′ unitape orientation and has low modulus in 90° directions because of the lack of fiber in that direction.

Laminate S45 preferably has a tricot knit on one side for added abrasion resistance and a non-breathable urethane membrane film W6−2.0 on the other side so that the laminate is waterproof-non breathable with fibers laid at about O″+45°, and −45° so the material (through the combination of the fiber angles and stretchable film and stretchable tricot) has low modulus in the 90′ direction.

Additional alternative surface coatings may include various types of knits, wovens, non-wovens, meshes, breathable films (porous and non porous), multilayered films, foams. Preferably, adding various materials, as noted, into the stack of plies in configurations other than described for instance: having a woven material between layers of unitape; having a film layer between unitape plies; having a woven material and a weldable film layer between two plies of unitape etc, may suffice.

Further, other preferred alternative fiber angles could be used to drive high modulus in fiber reinforced directions and low modulus in non-fiber reinforced directions (assuming flexible matrix and other non-fiber components are also low-modulus).

Upon reading this specification, those with ordinary skill in the art will now appreciate that, under appropriate circumstances, considering such issues as design preference, user preferences, marketing preferences, cost, structural requirements, available materials, technological advances, etc., other material arrangements such as, for example, material could be cured inside or outside an autoclave, exact material unitapes and other components may be changed to control the modulus of the material in off and on fiber axis directions, etc., may suffice.

And, upon reading this specification, those with ordinary skill in the art will now appreciate that, under appropriate circumstances, considering such issues as design preference, user preferences, marketing preferences, cost, structural requirements, available materials, technological advances, etc., other adhesive arrangements such as, for example, removing current surface coatings and utilizing ct71 to be both the adhesive and the coating, etc., may suffice. Alternately preferably, no adhesive may be needed if the fibers are weldable to themselves and/or the surface coatings.

Further, upon reading this specification, those with ordinary skill in the art will now appreciate that, under appropriate circumstances, considering such issues as design preference, user preferences, marketing preferences, cost, structural requirements, available materials, technological advances, etc., other materials and layering arrangements to improve performance and usability, such as those indicated below, may suffice:

-   -   i. Resin         -   1. toughening agents         -   2. breathable adhesive         -   3. non-breathable adhesive         -   4. FR additives         -   5. No-stink additives         -   6. Other resins             -   a. Water based             -   b. PU's     -   ii. thin films         -   1. breathable film         -   2. non breathable         -   3. directionally strong films     -   iii. texture could be added     -   iv. abrasion layers         -   1. woven nylon         -   2. woven polyester         -   3. non-wovens         -   4. super fabric     -   v. non-woven layers         -   1. on outer surface         -   2. between plies     -   vi. unitape fiber         -   1. fiber types             -   a. aramid             -   b. para aramid             -   c. Liquid Crystal Polymers             -   d. UHMEPE             -   e. Polyesters             -   f. Polyamides (Nylons)             -   g. Polybenzimidazole         -   2. Resin content             -   a. Increased             -   b. Decreased         -   3. Amount of fiber             -   a. Increased             -   b. Decreased         -   4. Unitape Fiber hybrids             -   a. Intra laminar             -   b. Inter laminar     -   vii. Ply count can change     -   viii. Unitape per ply can change     -   ix. Unitape directions can change

And, upon reading this specification, those with ordinary skill in the art will now appreciate that, under appropriate circumstances, considering such issues as design preference, user preferences, marketing preferences, cost, structural requirements, available materials, technological advances, etc., other uses such as, for example, medical bracing, safety devices (fall straps), etc., may suffice.

Although applicant has described applicant's preferred embodiments of this invention, it will be understood that the broadest scope of this invention includes modifications such as diverse shapes, sizes, and materials. Such scope is limited only by the below claims as read in connection with the above specification. Further, many other advantages of applicant's invention will be apparent to those skilled in the art from the above descriptions and the below claims. 

What is claimed is:
 1. A laminate comprising: a reinforcing element comprising three unidirectional tape layers bonded to one another, each unidirectional tape layer comprising parallel monofilaments disposed in a predetermined direction within a non-breathable partially thermoset adhesive; a first non-breathable weldable urethane membrane film layer bonded to a first side of the reinforcing element; and a second non-breathable weldable urethane membrane film layer bonded to a second side of the reinforcing element, opposite the first non-breathable weldable urethane membrane film layer, wherein the predetermined directions of the three unidirectional tape layers are at a 0°, +45°, and −45° orientation.
 2. The laminate of claim 1, wherein said monofilaments comprise ultra-high molecular weight polyethylene (UHMWPE).
 3. The laminate of claim 2, wherein each unidirectional tape layer comprises about 12 gsm to about 16 gsm of the non-breathable, partially thermosetting adhesive and from about 12 gsm to about 16 gsm of the UHMWPE monofilaments.
 4. The laminate of claim 1, wherein the laminate has a basis weight of about 215 gsm.
 5. The laminate of claim 1, wherein the monofilaments have diameters less than 20 microns, and wherein spacing between individual monofilaments within an adjoining strengthening group of monofilaments is within a gap distance in the range between non-abutting monofilaments up to nine times the monofilament major diameter.
 6. A three-dimensionally shaped, flexible composite part comprising the laminate according to claim
 1. 